The TEM and FESEM images showed that the completed nitridation product was primarily composed of nearly spherical AlN granules with sizes of 20–30 nm.

TEM和FESEM图像显示，完成的氮化产物主要由尺寸为20-30nm的近球形AlN颗粒组成。

Synthesis of highly sinterable AlN nanopowders through sol-gel route by reduction-nitridation in ammonia

More Spherical Aln 球形铝 sentence examples
10.7567/1347-4065/AB09D3

AlN film deposited with the PALE technique with the highest number of pulse cycles (1050) was observed to exhibit highly uniform spherical AlN grains and a dense film surface with a root mean square roughness of 0.

观察到用 PALE 技术沉积的具有最高脉冲周期数 (1050) 的 AlN 薄膜表现出高度均匀的球形 AlN 晶粒和致密的薄膜表面，均方根粗糙度为 0。

Effects of pulse cycle number on the quality of pulsed atomic-layer epitaxy AlN films grown via metal organic chemical vapor deposition

More Spherical Aln 球形铝 sentence examples
10.1016/J.CERAMINT.2019.03.129

The spherical AlN powder with perfect dispersibility was prepared after a heat treatment at 1550 °C for 2 h in flowing N2.

在流动的 N2 中，在 1550°C 热处理 2h 后，制备出具有良好分散性的球形 AlN 粉末。

Preparation of spherical AlN powders by combined microemulsion method and carbothermal method

Learn more from Spherical Aln 球形铝

Keywords related to Spherical

Spherical Aln 球形铝

Spherical Aln 球形铝
Encyclopedia 百科全书

Spherical Aln(球形铝)研究综述

Spherical Aln 球形铝 - The TEM and FESEM images showed that the completed nitridation product was primarily composed of nearly spherical AlN granules with sizes of 20–30 nm. [1] AlN film deposited with the PALE technique with the highest number of pulse cycles (1050) was observed to exhibit highly uniform spherical AlN grains and a dense film surface with a root mean square roughness of 0. [2] The spherical AlN powder with perfect dispersibility was prepared after a heat treatment at 1550 °C for 2 h in flowing N2. [3]
TEM和FESEM图像显示，完成的氮化产物主要由尺寸为20-30nm的近球形AlN颗粒组成。 [1] 观察到用 PALE 技术沉积的具有最高脉冲周期数 (1050) 的 AlN 薄膜表现出高度均匀的球形 AlN 晶粒和致密的薄膜表面，均方根粗糙度为 0。 [2] 在流动的 N2 中，在 1550°C 热处理 2h 后，制备出具有良好分散性的球形 AlN 粉末。 [3]