Ybco Films(Ybco 필름)란 무엇입니까?
Ybco Films Ybco 필름 - a value among the highest ever reported in YBCO films. [1] This test method can be used for the rapid and non-destructive detection of residual stress in YBCO films. [2] The experimental results and constructed theoretical models help us to understand the characteristics of flux avalanche in YBCO films and are of significance to evaluate the flux stability for practical applications of high temperature superconducting films. [3] In addition, the surface of the LMO layer during the magnetron sputtering process is improved via controlling the O2 flux, and then the critical-current density (Jc) of YBCO films has been improved. [4] Effects of yttrium oxide inclusions on the orientation and superconducting properties of YBCO films. [5] Failure of yttrium barium copper oxide (YBCO) coated conductors (CC) tapes usually manifests as delamination occurring majorly in the YBCO films. [6] We performed a complete texture analysis and proposed a qualitative texture model explaining the measured X-ray pole figures of the YBCO films. [7] We investigated the influence of the growing temperatures on both the microstructure and superconducting properties of YBCO films by using conventional thermal annealing and flash-heating approaches. [8] Angular behaviors of critical current densityYBCO 영화에서 보고된 가장 높은 값 중 하나입니다. [1] 이 테스트 방법은 YBCO 필름의 잔류 응력을 빠르고 비파괴적으로 감지하는 데 사용할 수 있습니다. [2] 실험 결과와 구성된 이론적 모델은 YBCO 박막에서 자속 사태의 특성을 이해하는 데 도움이 되며 고온 초전도 박막의 실제 적용을 위한 자속 안정성을 평가하는 데 중요합니다. [3] 또한, 마그네트론 스퍼터링 공정 중 LMO 층의 표면은 O2 플럭스를 제어하여 개선되었으며, 그 결과 YBCO 필름의 임계 전류 밀도(Jc)가 개선되었습니다. [4] YBCO 필름의 배향 및 초전도 특성에 대한 이트륨 산화물 개재물의 효과. [5] 이트륨 바륨 구리 산화물(YBCO) 코팅 전도체(CC) 테이프의 고장은 일반적으로 YBCO 필름에서 주로 발생하는 박리로 나타납니다. [6] 우리는 완전한 텍스처 분석을 수행하고 YBCO 필름의 측정된 X선 극점 수치를 설명하는 정성적 텍스처 모델을 제안했습니다. [7] 우리는 기존의 열처리 및 플래시 가열 방식을 사용하여 YBCO 필름의 미세 구조 및 초전도 특성에 대한 성장 온도의 영향을 조사했습니다. [8] 77K, 1T에서 임계 전류 밀도 <italic>J</italic><sub>c</sub> 및 <italic>n</italic>-값의 각도 거동을 기둥형 결함(CD)이 있는 YBCO 필름에서 조사했습니다. CD가 중이온 조사에 의해 설치된 다른 각도에서 CD를 추가로 도입하기 전과 후에 <italic>ab</italic> 평면에 대해 작은 각도로 기울어졌습니다. [9] YBCO 필름에서 플럭스 피닝의 분자 역학(MD) 시뮬레이션과 결합된 Jc의 실험적으로 측정된 각도 종속성을 기반으로 인공적으로 YBCO 필름 매트릭스에 도입된 BZO 나노로드의 스프레잉 및 단편화가 대다수를 설명하는 정량적 모델을 제시합니다. 관찰된 임계 전류 이방성. [10] 이 연구에서는 YBCO 필름의 플럭스 피닝 성능을 크게 향상시킬 수 있는 쉽고 효과적인 방법이 보고되었습니다. [11] 낮은 불소 전구체 용액을 사용하여 금속-유기 분해(MOD)에 의해 유도된 YBCO 필름은 베어 및 BZO로 장식된 STO 기판 모두에서 성공적으로 성장되었습니다. [12] 따라서 인공 피닝 센터가 있는 YBCO 필름의 현장 임계 전류 이방성을 해석할 때 집단 개인 및 다중 소용돌이 고정의 메커니즘이 중요한 역할을 하는 것으로 관찰되었습니다. [13] 초전도 돔의 대부분에 걸쳐 있는 몇 개의 단위 셀과 산소 도핑 수준으로 두께를 낮출 수 있는 YBCO 필름은 50nm 이하의 치수를 갖는 나노와이어로 패턴화됩니다. [14] % Y<sub>2</sub>O<sub>3</sub> 도핑(DD) YBCO 필름. [15] 따라서 BCO 나노닷은 금속 기판 위의 YBCO 필름의 스레딩 전위 외에 플럭스 피닝을 개선하는 데 사용할 수 있습니다. [16] YBCO 필름은 SEM, X선 회절(XRD), 투과 전자 현미경(TEM), DC 저항률 및 임계 전류 측정을 통해 특성화되었습니다. [17] 이 논문에서는 다음 세 가지 항목에 중점을 둡니다. 1) YBa<sub>2</sub>Cu<의 표면 저항(<italic>R</italic><sub>s</sub>)의 영향 NMR 픽업 코일의 <이탤릭>Q</sub>에 있는 sub>3</sub>O<sub>7-δ</sub>(YBCO) 필름; 2) 코일 선폭과 코일에 흐르는 전류의 관계 및 3) NMR 픽업 코일의 Q에 대한 YBCO 필름에 대한 Si 이온 조사의 영향. [18] 우리의 이전 연구에서 발견된 바와 같이 전구체 용액에 아세트산납을 첨가하면 a/b축 방향 결정립의 악화를 억제할 수 있기 때문에 YBCO 필름의 임계 전류 밀도를 향상시킬 수 있습니다. [19] BZO 나노 입자를 포함하거나 포함하지 않은 YBCO 필름의 임계 전류 밀도(Jc) 성능을 비교함으로써 840°C 증착된 BZO-YBCO는 7의 더 높은 Jc 값을 분명히 나타냅니다. [20] YBCO 필름은 NdGaO<sub>3</sub> 기질을 사용하여 공기 중에서 액상 에피택시에 의해 준비되었습니다. [21]
Doped Ybco Films 도핑된 Ybco 필름
Moreover, the sectional microstructures of the YBCO superconducting layer observed by a field emission transmission electron microscope show the columnar defects with the size of about 9 nm form in the doped YBCO films after the irradiation, confirming traces of continuous latent tracks exist as the evidence of effective mixed-pinning landscapes. [1] Here, we report an efficient mixed-pinning landscape for enhancing the in-field performance of BaTiO3 (BTO)-doped YBCO films by low-energy (60 keV) proton irradiation. [2] This comprehensive study leads to an additional intermediate dwelling step during thermal process to increase the YBCO nuclei density before the YBCO growth, resulting to a self-field J(c) of 5-6MA/cm(2) at 77K for undoped and ZrO2-doped YBCO films. [3]또한, 전계방출 투과형 전자현미경으로 관찰된 YBCO 초전도층의 단면 미세구조는 조사 후 도핑된 YBCO 막에 약 9 nm 크기의 기둥형 결함을 보여 연속적인 잠복궤적의 흔적이 존재함을 확인시켜준다. 효과적인 혼합 피닝 풍경. [1] 여기에서 우리는 저에너지(60keV) 양성자 조사에 의해 BaTiO3(BTO) 도핑된 YBCO 필름의 현장 성능을 향상시키기 위한 효율적인 혼합 피닝 환경을 보고합니다. [2] 이 포괄적인 연구는 YBCO 성장 전에 YBCO 핵 밀도를 증가시키기 위한 열처리 동안 추가적인 중간 거주 단계로 이어지며, 결과적으로 도핑되지 않은 ZrO2 및 ZrO2-에 대해 77K에서 5-6MA/cm(2)의 자체 필드 J(c)가 생성됩니다. 도핑된 YBCO 필름. [3]
Grown Ybco Films
Based on the rapidly pyrolyzed films, high-temperature firing process was further optimized to fabricate epitaxially grown YBCO films. [1] The YBCO SQUIDs are based on grain boundary Josephson junctions and are patterned in a single layer of epitaxially grown YBCO films by Ga focused ion beam milling. [2]빠르게 열분해된 필름을 기반으로 고온 소성 공정을 더욱 최적화하여 에피택셜 성장된 YBCO 필름을 제조했습니다. [1] YBCO SQUID는 입자 경계 Josephson 접합을 기반으로 하며 Ga 집중 이온 빔 밀링에 의해 에피택셜 성장된 YBCO 필름의 단일 층에 패턴화됩니다. [2]
Sided Ybco Films
5-mm thick MgO wafer with double-sided YBCO films demonstrates 1-dB cut-off frequency (fc) at 2 GHz and 0. [1] 5mm-thick MgO wafer with double sided YBCO films. [2]양면 YBCO 필름이 있는 5mm 두께의 MgO 웨이퍼는 2GHz 및 0에서 1dB 차단 주파수(fc)를 보여줍니다. [1] 양면 YBCO 필름이 있는 5mm 두께의 MgO 웨이퍼. [2]
ybco films prepared
In this work, we present the influence of different decomposition time for the YBCO films prepared by the precursor solutions with three F/Ba mole ratios of 6:1, 2:1, and 1:1 (the fluorine contents are 28. [1] Coaddition of Br and metals (이 작업에서 우리는 6:1, 2:1 및 1:1의 세 가지 F/Ba 몰비(불소 함량은 28)로 전구체 용액에 의해 제조된 YBCO 필름에 대한 다양한 분해 시간의 영향을 제시합니다. [1] Br과 금속(<italic>M</italic>)의 결합(여기서 <italic>M</italic> = Zr, Sn, Hf)은 fluorine-free 금속-유기 분해 방법으로 제조된 YBCO 필름에 대해 시도되었습니다. [2]