Whisker Reinforced(강화된 수염)란 무엇입니까?
Whisker Reinforced 강화된 수염 - Herein, in-situ synthesized MgAlB4 whisker reinforced Al (MgAlB4w/Al) composites with rational distribution of the reinforcement were successfully prepared by an efficient process combining vacuum pressureless sintering and hot-extrusion. [1] In this regard, silica fume of various contents was added to plain concrete (PC), CaCO3 whisker reinforced cementitious composites (CWRCC) and basalt fiber reinforced cementitious composites (BFRC). [2] The current work suggests that HOP could be an effective technique for the preparation of whisker reinforced ceramic composites. [3] This paper prepared magnesium borate whisker reinforced aluminum matrix composites by extrusion casting, and studied the effects of the volume fraction of the reinforced phase on the mechanical properties, thermal expansion properties and microstructure of the composites. [4] Aiming at developing high temperature resistance aluminum matrix composites for both structural and functional purposes, the novel MgAlB4 whisker reinforced Al matrix composites with directional distributed reinforcement were fabricated using powder metallurgy followed by hot extrusion. [5] Al2O3 f/Al-Si composites and aluminum borate whisker reinforced Al-Si matrix composites exhibited higher anti-ablation properties, which contributed by the dense structure and high yield strength at high temperature of the composites. [6] The improvement in wear resistance of the ceramic whisker reinforced coatings could be mainly due to the interlocking interface between splats and decrease of intralamellar cracks in the top coat. [7] In addition, during the HS milling process, this characteristic was also presented on the failure faces of homogeneous tool with SiC whisker reinforced. [8] This work investigated the influences of two-step shot peening on the residual stress fields, microstructure, microhardness and corrosion performance of aluminum borate (Al18B4O33) whisker reinforced Al Mg Si matrix composite by X-ray stress tester, X-ray diffraction line profile analysis method, transmission electron microscopy (TEM), Vickers analyzer and electrochemical examinations, respectively. [9] The performance of PVD TiAlN coated carbide, whisker reinforced ceramic and cubic boron nitride cBN inserts had been evaluated in terms of cutting force encountered during machining, flank wear developed on the tool and surface roughness on the machined component. [10] A commercial carbon whisker reinforced polylactic acid composite made by a type of three-dimensional (3D) printing known as material extrusion additive manufacturing is investigated. [11]여기에서, 강화재의 합리적인 분포를 가진 제자리 합성 MgAlB4 위스커 강화 Al(MgAlB4w/Al) 복합재가 진공 무압 소결과 열간 압출을 결합한 효율적인 공정에 의해 성공적으로 준비되었습니다. [1] 이와 관련하여 일반 콘크리트(PC), CaCO3 위스커 강화 시멘트질 복합재(CWRCC) 및 현무암 섬유 강화 시멘트질 복합재(BFRC)에 다양한 함량의 실리카흄을 첨가하였다. [2] 현재 작업은 HOP가 위스커 강화 세라믹 복합 재료의 준비를 위한 효과적인 기술이 될 수 있음을 시사합니다. [3] 본 논문에서는 붕산마그네슘 휘스커 강화 알루미늄 기지 복합재료를 압출주조법으로 제조하고 강화상의 체적분율이 복합재료의 기계적 특성, 열팽창 특성 및 미세구조에 미치는 영향을 연구하였다. [4] 구조적 및 기능적 목적 모두를 위한 고온 저항 알루미늄 기지 복합재 개발을 목표로, 방향성 분포 강화가 있는 새로운 MgAlB4 위스커 강화 Al 기지 복합재가 분말 야금과 열간 압출을 사용하여 제작되었습니다. [5] Al2O3f/Al-Si 복합재와 알루미늄 붕산염 위스커 강화 Al-Si 매트릭스 복합재는 더 높은 내삭마 특성을 나타냈으며, 이는 복합재의 고온에서 조밀한 구조와 높은 항복 강도에 기여했습니다. [6] 세라믹 위스커 강화 코팅의 내마모성 향상은 주로 스플랫 사이의 맞물림 경계면과 상도의 라멜라 내 균열 감소로 인한 것일 수 있습니다. [7] 또한, HS 밀링 공정 중에 SiC 휘스커가 강화된 균질 공구의 파손면에서도 이러한 특성이 나타났습니다. [8] 본 연구는 X선 응력 시험기, X선 회절선 프로파일 분석을 통해 알루미늄 붕산염(Al18B4O33) 위스커 강화 Al Mg Si 매트릭스 복합재의 잔류 응력장, 미세 구조, 미세 경도 및 부식 성능에 대한 2단계 쇼트 피닝의 영향을 조사했습니다. 방법, 투과전자현미경(TEM), Vickers 분석기 및 전기화학적 검사 각각. [9] PVD TiAlN 코팅 카바이드, 위스커 강화 세라믹 및 입방정 질화붕소 cBN 인서트의 성능은 가공 중 발생하는 절삭력, 공구에서 발생하는 측면 마모 및 가공된 부품의 표면 거칠기 측면에서 평가되었습니다. [10] 재료 압출 적층 제조로 알려진 일종의 3D 프린팅으로 만든 상업용 탄소 위스커 강화 폴리락트산 복합재가 조사되었습니다. [11]
Borate Whisker Reinforced
This paper prepared magnesium borate whisker reinforced aluminum matrix composites by extrusion casting, and studied the effects of the volume fraction of the reinforced phase on the mechanical properties, thermal expansion properties and microstructure of the composites. [1] Al2O3 f/Al-Si composites and aluminum borate whisker reinforced Al-Si matrix composites exhibited higher anti-ablation properties, which contributed by the dense structure and high yield strength at high temperature of the composites. [2]본 논문에서는 붕산마그네슘 휘스커 강화 알루미늄 기지 복합재료를 압출주조법으로 제조하고 강화상의 체적분율이 복합재료의 기계적 특성, 열팽창 특성 및 미세구조에 미치는 영향을 연구하였다. [1] Al2O3f/Al-Si 복합재와 알루미늄 붕산염 위스커 강화 Al-Si 매트릭스 복합재는 더 높은 내삭마 특성을 나타냈으며, 이는 복합재의 고온에서 조밀한 구조와 높은 항복 강도에 기여했습니다. [2]
Mgalb4 Whisker Reinforced Mgalb4 수염 강화
Herein, in-situ synthesized MgAlB4 whisker reinforced Al (MgAlB4w/Al) composites with rational distribution of the reinforcement were successfully prepared by an efficient process combining vacuum pressureless sintering and hot-extrusion. [1] Aiming at developing high temperature resistance aluminum matrix composites for both structural and functional purposes, the novel MgAlB4 whisker reinforced Al matrix composites with directional distributed reinforcement were fabricated using powder metallurgy followed by hot extrusion. [2]여기에서, 강화재의 합리적인 분포를 가진 제자리 합성 MgAlB4 위스커 강화 Al(MgAlB4w/Al) 복합재가 진공 무압 소결과 열간 압출을 결합한 효율적인 공정에 의해 성공적으로 준비되었습니다. [1] 구조적 및 기능적 목적 모두를 위한 고온 저항 알루미늄 기지 복합재 개발을 목표로, 방향성 분포 강화가 있는 새로운 MgAlB4 위스커 강화 Al 기지 복합재가 분말 야금과 열간 압출을 사용하여 제작되었습니다. [2]
whisker reinforced al 수염 강화 알
Herein, in-situ synthesized MgAlB4 whisker reinforced Al (MgAlB4w/Al) composites with rational distribution of the reinforcement were successfully prepared by an efficient process combining vacuum pressureless sintering and hot-extrusion. [1] Aiming at developing high temperature resistance aluminum matrix composites for both structural and functional purposes, the novel MgAlB4 whisker reinforced Al matrix composites with directional distributed reinforcement were fabricated using powder metallurgy followed by hot extrusion. [2] Al2O3 f/Al-Si composites and aluminum borate whisker reinforced Al-Si matrix composites exhibited higher anti-ablation properties, which contributed by the dense structure and high yield strength at high temperature of the composites. [3] This work investigated the influences of two-step shot peening on the residual stress fields, microstructure, microhardness and corrosion performance of aluminum borate (Al18B4O33) whisker reinforced Al Mg Si matrix composite by X-ray stress tester, X-ray diffraction line profile analysis method, transmission electron microscopy (TEM), Vickers analyzer and electrochemical examinations, respectively. [4]여기에서, 강화재의 합리적인 분포를 가진 제자리 합성 MgAlB4 위스커 강화 Al(MgAlB4w/Al) 복합재가 진공 무압 소결과 열간 압출을 결합한 효율적인 공정에 의해 성공적으로 준비되었습니다. [1] 구조적 및 기능적 목적 모두를 위한 고온 저항 알루미늄 기지 복합재 개발을 목표로, 방향성 분포 강화가 있는 새로운 MgAlB4 위스커 강화 Al 기지 복합재가 분말 야금과 열간 압출을 사용하여 제작되었습니다. [2] Al2O3f/Al-Si 복합재와 알루미늄 붕산염 위스커 강화 Al-Si 매트릭스 복합재는 더 높은 내삭마 특성을 나타냈으며, 이는 복합재의 고온에서 조밀한 구조와 높은 항복 강도에 기여했습니다. [3] 본 연구는 X선 응력 시험기, X선 회절선 프로파일 분석을 통해 알루미늄 붕산염(Al18B4O33) 위스커 강화 Al Mg Si 매트릭스 복합재의 잔류 응력장, 미세 구조, 미세 경도 및 부식 성능에 대한 2단계 쇼트 피닝의 영향을 조사했습니다. 방법, 투과전자현미경(TEM), Vickers 분석기 및 전기화학적 검사 각각. [4]
whisker reinforced ceramic
The current work suggests that HOP could be an effective technique for the preparation of whisker reinforced ceramic composites. [1] The performance of PVD TiAlN coated carbide, whisker reinforced ceramic and cubic boron nitride cBN inserts had been evaluated in terms of cutting force encountered during machining, flank wear developed on the tool and surface roughness on the machined component. [2]현재 작업은 HOP가 위스커 강화 세라믹 복합 재료의 준비를 위한 효과적인 기술이 될 수 있음을 시사합니다. [1] PVD TiAlN 코팅 카바이드, 위스커 강화 세라믹 및 입방정 질화붕소 cBN 인서트의 성능은 가공 중 발생하는 절삭력, 공구에서 발생하는 측면 마모 및 가공된 부품의 표면 거칠기 측면에서 평가되었습니다. [2]