Ssz 13 Membranes
Sz 13 멤브레인

Sentence Examples

Discover more insights into Ssz 13 Membranes Sz 13 멤브레인

Keywords frequently search together with Ssz 13 Membranes Sz 13 멤브레인

Narrow sentence examples with built-in keyword filters

More Ssz 13 Membranes Sz 13 멤브레인 sentence examples
10.1016/J.MEMSCI.2021.119297

In this study, SSZ-13 membranes were prepared by a hot-dipping method, where the hot contact of seeded support and mother liquor at synthesis temperature resulted into fast crystallization kinetics and thin membranes.

이 연구에서 SSZ-13 멤브레인은 합성 온도에서 종자 지지체와 모액의 뜨거운 접촉으로 인해 빠른 결정화 속도와 얇은 멤브레인이 생성되는 용융 침지 방법으로 제조되었습니다.

Fast synthesis of thin SSZ-13 membranes by a hot-dipping method

More Ssz 13 Membranes Sz 13 멤브레인 sentence examples
10.1016/J.MEMSCI.2021.119565

8 A) of bilayer silicalite-1/SSZ-13 membranes guarantee the separation efficiency.

8A) 이중층 실리카라이트-1/SSZ-13 막은 분리 효율을 보장합니다.

Highly CO2-selective and moisture-resistant bilayer silicalite-1/SSZ-13 membranes with gradient pores for wet CO2/CH4 and CO2/N2 separations

More Ssz 13 Membranes Sz 13 멤브레인 sentence examples
10.1016/J.MEMSCI.2021.119349

Herein, high-quality and N2-selective SSZ-13 membranes on α-alumina tubes were prepared using a novel synthesis approach called seeded-gel synthesis.

여기에서 α-알루미나 튜브의 고품질 N2 선택성 SSZ-13 멤브레인은 seeded-gel 합성이라는 새로운 합성 방법을 사용하여 준비되었습니다.

A facile approach to synthesize SSZ-13 membranes with ultrahigh N2 permeances for efficient N2/CH4 separations

Learn more from Ssz 13 Membranes Sz 13 멤브레인

Keywords related to Membranes

Ssz 13 Membranes Sz 13 멤브레인

Ssz 13 Membranes Sz 13 멤브레인
Encyclopedia 백과사전

Ssz 13 Membranes(Sz 13 멤브레인)란 무엇입니까?

Ssz 13 Membranes Sz 13 멤브레인 - In this study, SSZ-13 membranes were prepared by a hot-dipping method, where the hot contact of seeded support and mother liquor at synthesis temperature resulted into fast crystallization kinetics and thin membranes. [1] 8 A) of bilayer silicalite-1/SSZ-13 membranes guarantee the separation efficiency. [2] Herein, high-quality and N2-selective SSZ-13 membranes on α-alumina tubes were prepared using a novel synthesis approach called seeded-gel synthesis. [3]
이 연구에서 SSZ-13 멤브레인은 합성 온도에서 종자 지지체와 모액의 뜨거운 접촉으로 인해 빠른 결정화 속도와 얇은 멤브레인이 생성되는 용융 침지 방법으로 제조되었습니다. [1] 8A) 이중층 실리카라이트-1/SSZ-13 막은 분리 효율을 보장합니다. [2] 여기에서 α-알루미나 튜브의 고품질 N2 선택성 SSZ-13 멤브레인은 seeded-gel 합성이라는 새로운 합성 방법을 사용하여 준비되었습니다. [3]