Thermosetting Polyurethane 熱硬化性ポリウレタン - A series of solid–solid phase-change material (SSPCM) of thermosetting polyurethane (TPU) nanoarrays were successfully fabricated by in situ polymerization of poly(ethylene glycol) (PEG)-containing macromonomers in nanoporous alumina (anodized aluminum oxide, AAO) templates. [1] In this paper, we designed a convenient strategy to achieve 3D shape-changings of thermosetting polyurethane (PU) with the aid of Near Infrared (NIR) light, including temporary and permanent shapes. [2] Thermosetting polyurethanes (PUs) with the enhanced mechanical properties were facilely prepared without the catalysts by a simple two-step method. [3] Graphene nanoplatelets (xGnP), expanded graphite (EG), multiwall carbon nanotubes (MWCNTs), and carbon black (CB) were dispersed in various amounts in a thermosetting polyurethane (PU) matrix derived from castor oil and composite plaques were obtained by compression molding. [4]熱硬化性ポリウレタン（TPU）ナノアレイの一連の固相-固相相変化材料（SSPCM）は、ナノポーラスアルミナ（陽極酸化アルミニウム、AAO）テンプレートでのポリ（エチレングリコール）（PEG）含有マクロモノマーのinsitu重合によって正常に製造されました。 。 [1] この論文では、一時的および永続的な形状を含む、近赤外線（NIR）光を利用して、熱硬化性ポリウレタン（PU）の3D形状変化を実現するための便利な戦略を設計しました。 [2] 機械的特性が強化された熱硬化性ポリウレタン（PU）は、触媒なしで簡単な2段階の方法で簡単に調製できました。 [3] グラフェンナノプレートレット（xGnP）、発泡グラファイト（EG）、多層カーボンナノチューブ（MWCNT）、およびカーボンブラック（CB）を、ヒマシ油由来の熱硬化性ポリウレタン（PU）マトリックスにさまざまな量で分散させ、圧縮成形によって複合プラークを得ました。 。 [4]