ポリベンゾイミダゾール膜とは何ですか？
Polybenzimidazole Membranes ポリベンゾイミダゾール膜 - The main objectives of this review paper are as follows: (1) the latest development of the HT-PEMs, primarily based on polybenzimidazole membranes and (2) the latest development of the fuel cell performance and the lifetime of the HT-PEMs. [1] Polybenzimidazole membranes with dual proton transport channels (B-PBI) are designed and fabricated for vanadium flow battery (VFB) applications. [2] Herein, a new approach is reported to avoid this cost by balancing electrolyte transport with amphoteric bilayer Nafion/meta-polybenzimidazole membranes. [3] But the proton conductivity of polybenzimidazole membranes is just moderate; the vanadium redox flow battery assembled with polybenzimidazole membranes usual cannot achieve satisfactory voltage efficiency. [4]このレビューペーパーの主な目的は次のとおりです。（1）主にポリベンズイミダゾール膜に基づくHT-PEMの最新の開発、および（2）燃料電池の性能とHT-PEMの寿命の最新の開発。 [1] デュアル プロトン輸送チャネル (B-PBI) を持つポリベンズイミダゾール膜は、バナジウム フロー電池 (VFB) アプリケーション用に設計および製造されています。 [2] ここでは、電解質輸送と両性二重層ナフィオン/メタ-ポリベンズイミダゾール膜のバランスを取ることにより、このコストを回避する新しいアプローチが報告されています。 [3] しかし、ポリベンズイミダゾール膜のプロトン伝導率は中程度です。通常、ポリベンズイミダゾール膜で組み立てられたバナジウム レドックス フロー電池は、十分な電圧効率を達成できません。 [4]
Doped Polybenzimidazole Membranes
3 Å showed a significant siphoning effect as confirmed by the delocalization of PA in 31P NMR, thus allowing high retention of PA even under highly humidified conditions and presenting more than three orders of magnitude higher proton conductivity retention than conventional dense PA-doped polybenzimidazole membranes (PBI/PA). [1] Demonstration cells based on KOH doped polybenzimidazole membranes and nickel based electrodes exhibited 1700 mA cm−2 at 1. [2] This work presents the first durability studies of vapor-fed direct dimethyl ether fuel cells with phosphoric acid doped polybenzimidazole membranes as electrolytes. [3] The degradation pathway of phosphoric acid doped polybenzimidazole membranes in high temperature polymer electrolyte membrane fuel cells depends on the acid contents. [4]3Åは、31P NMRでのPAの非局在化によって確認されるように、有意なサイフォン効果を示しました。したがって、高度に加湿された条件下でもPAの高い保持を可能にし、従来の高密度PAドープポリベンズイミダゾール膜よりも3桁以上高いプロトン伝導性保持を示します（ PBI / PA）。 [1] KOH をドープしたポリベンズイミダゾール膜とニッケルベースの電極に基づく実証セルは、1 で 1700 mA cm-2 を示しました。 [2] この研究は、リン酸をドープしたポリベンズイミダゾール膜を電解質として使用した、蒸気供給直接ジメチルエーテル燃料電池の最初の耐久性研究を示しています。 [3] 高温高分子電解質膜燃料電池におけるリン酸ドープポリベンズイミダゾール膜の分解経路は、酸含有量に依存します。 [4]